Customization: | Available |
---|---|
Application: | Communication |
Type: | Single-Mode or Multimode Fiber |
Still deciding? Get samples of US$ 0.1/Meter
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Cable Type | GYFTY |
Fiber Type | G652D |
Application | Long-distance communication, LAN |
Recommended installation methods | Aerial |
Environment | Outdoor |
Temperature Range | -40ºC to 70ºC |
Technical data: |
||||||||
Fiber Num. | Outer diameter (mm) | Weight (kg/km) | Min.Bending radius(mm) | Tension (N) | Crash loading (N/100mm) | |||
Static | Dynamic | Short term | Long term | Short term | Long term | |||
2-36 | 10.4 | 90 | 10 times O.D. | 20 times O.D. | 1500 | 600 | 1000 | 300 |
38-60 | 10.2 | 110 | ||||||
62-72 | 11.7 | 115 | ||||||
74-96 | 13.4 | 150 | ||||||
98-120 | 15.0 | 190 | ||||||
122-144 | 16.6 | 230 | ||||||
146-216 | 16.9 | 240 | ||||||
218-240 | 19.3 | 305 | ||||||
242-288 | 21.5 | 375 |
Technical parameter of ITU-T G.652D (B1.3) single-mode optical fiber | |||
Optical Characteristics | |||
Mode field diameter (MFD) | 1310nm 1550nm |
9.2±0.4 10.4±0.8 |
µm µm |
Cut-off wavelength (λcc) | ≤1260 | nm | |
Attenuation coefficient | 1310nm 1383nm 1550nm |
<0.35 <0.35 <0.22 |
dB/km dB/km dB/km |
Macro bending loss | φ75mm, 100circles, at 1550nm | ≤0.1 | dB |
Attenuation non-uniformity | ≤0.05 | dB | |
Dispersion coefficient | 1288~1339nm 1271~1360nm 1550nm |
≤3.5 ≤5.3 ≤18 |
Ps/(nm.km) Ps/(nm.km) Ps/(nm.km) |
Zero dispersion wavelength | 1300~1324 | nm | |
Max zero dispersion slope | ≤0.093 | Ps/(nm2.km) | |
Group index of refraction (typical value) | 1310nm 1550nm |
1.466 1.467 |
|
Geometric characteristic | |||
Cladding diameter | 125.0±1.0 | µm | |
Core/cladding concentricity error | ≤0.8 | µm | |
Cladding non-circularity | ≤1.0 | % | |
Coating diameter | 245.0±10 | µm | |
Cladding/coating concentricity error | ≤12.0 | µm | |
Coating non-circularity | ≤8 | % | |
Diameter of colored coating | 250.0±15 | µm | |
Mechanical characteristic | |||
Curling (radius) | ≥4 | m | |
Proof stress | >0.69 | Gpa | |
Coating strip force | Average value Peak value |
1.0-5.0 1.3-8.9 |
N N |
Dynamic stress corrosion susceptibility parameter (nd value) | ≥20 |